Various requests such as adding special functions etc. We will solve this problem using the impregnation technology that we have cultivated over many years. Please feel free to contact us.
Lay Seal 100
Impregnants for rapid prototyping parts
Market
-
Powder Shaped material
Purpose
- Sealing
- Adding pressure resistance
- Pre-treatment for suface treatment
Features
This product has high adhesion to resin and is suitable for relatively large gaps and holes.
| Main component | Methacrylic acid ester (water insoluble) |
|---|---|
| Appearance | Transparent liquid |
| Target material | Metal / Resin |
| Pressure resistance | 2.0 MPa or more |
| Active ingredient | 100%（Penetration is 100% cured） |
| Density(25℃) | 1.08～1.10 g/cm3 |
| Viscosity(25℃) | 60～70 mPa・s |
| How to use | Add the entire amount of hardening agent to the base resin and stir thoroughly before use. |
| Storage method | Cool and dark place below 20℃ |
| Packing style | Main agent ：Lami clean can Hardening agent：Lamizip |
How to use
- Impregnation process Vacuuming ⇒ Liquid filling ⇒ Re-vacuum ⇒ Pressurization
- Washing process Hot water wash
- Curing process Harden in boiling water
Lay Seal 150 / 153 / 155 / 160
Adhesive and Impregnants for electrical steel sheets and laminated cores.
Market
-
Electromagnetic Steel Plate/
Laminated core
Purpose
- Sealing
- Adhesion
- Vibration suppression
- Reducing iron loss
Features
This is an acrylic solvent-free impregnated adhesive developed to suppress vibrations in laminated cores and reduce iron loss. It has a low viscosity specification and is easy to handle, and is also compatible with vacuum impregnation, so it can penetrate almost 100% of the gaps between laminated layers and bond them.
| Products name | Lay Seal 150 | Lay Seal 153 | Lay Seal 155 | Lay Seal 160 |
|---|---|---|---|---|
| Main Component | （Meth）acrylic ester（water insoluble） | |||
| Appearance | Transparent liquid / Light yellow | |||
| Target material | Electrical steel sheet/ Amorphous / Other metals | |||
| Active ingredient | 100%（Penetration is 100% cured） | |||
| Density(25℃) | 1.06～1.08 g/cm3 | 1.06～1.08 g/cm3 | 1.05～1.08 g/cm3 | 1.05～1.08 g/cm3 |
| Viscosity(25℃) | 10～15 mPa・s | 10～15 mPa・s | 15～20 mPa・s | 20～25 mPa・s |
| Tensile shear adhesive strength test | 3～10 MPa | 5～10 MPa | 10～15 MPa | 20 MPa or more |
| Linear expansion coefficient | 1.79×10-4 /℃ | 1.75×10-4 /℃ | 1.79×10-4 /℃ | 1.65×10-4 /℃ |
| Decomposition temperature | 210 ℃ | 220 ℃ | 220 ℃ | 280 ℃以上 |
| Regular use heat resistant | 170 ℃ | 180 ℃ | 180 ℃ | 200 ℃ |
| How to use | Add the entire amount of hardening agent to the base resin and stir thoroughly before use. | |||
| Storage method | Cool, dark place (store at room temperature) | |||
| Packing style | Main agent：Lamiclean can Hardening agent：Lamizip |
|||
How to use
- Impregnation process Vacuum ⇒ Liquid filling ⇒ Pressure
- Washing process Air blow and tilting
- Curing process Gas phase 140℃ x 2 hours (temperature and time can be changed)
Mega Seal 200
Impregnants for thermal spray coatings
Market
Insulated bearing/ Thermal sprayed coating/Ceramic
Purpose
- Provides insulation
- Adding presure resistance
- Protection of base material against corrosive gases
- High heat resistant application parts
Features
By infiltrating a highly insulating and highly durable Impregnants into the small gaps in the thermal spray coating, dielectric breakdown is suppressed and the base material is protected. In addition, the Impregnants's low viscosity allows it to penetrate deep into the details and is highly effective.
| Main component | Methacrylic acid ester (water insoluble) |
|---|---|
| Appearance | Transparent liquid |
| Target material | Metal / Ceramic |
| Pressure resistance | 2.0 MPa or more |
| Active ingredient | 100%（Penetration is 100% cured） |
| Density(25℃) | 1.05～1.07 g/cm3 |
| Viscosity(25℃) | 20 mPa・s |
| Dielectric breakdown | 6,000 V No dielectric breakdown |
| Insulation resistance value | 1,000,000 MΩ or more |
| How to use | Add the entire amount of hardening agent to the base resin and stir thoroughly before use |
| Storage method | Cool and dark place below 20℃ |
| Packing style | Main agent：Lamiclean can Hardening agent：Lamizip |
How to use
- Impregnation process Vacuum ⇒ Liquid filling ⇒ Pressure
- Washing process Air blow/tilting
- Curing process Gas phase 140℃ x 2 hours (temperature and time can be changed)